Jafar Tahar Al-haidary, Ali Munder Mastafa and Ahmed Aziz Hamza
Cu-13Al-0.545Be shape memory alloy are heat treatment at different temperature and time. The microstructure of alloy after heat treatment at 850°C, 650°C and aging at 150°C ,450°C and 550°C for 2, 4 and 6 h study by optical microscope and X-ray diffraction. Bending test is use to show effect of heat treatment on super-elastic and shape memory effect.
Micro hardness test used to show effect of heat treatment on micro hardness .shape memory effect increase at heat treatment 650°C and aging at 150°C, while at 450°C and 550°C will decrease because precipitate formation rate rises with increase in temperature and time. The hardness and precipitates in the alloy increases with increasing ageing duration. Higher ageing temperature avoids the imperfection by moving and filling the empty space thereby hardens the alloy.