    Low-Cycle Fatigue Behaviors of Pre-Corroded Q345R Steel under Wet H2S Environments
    Author(s): Luo Yun-Rong, Fu Lei, Zeng Tao, Lin Haibo and Chen YanqiangLuo Yun-Rong, Fu Lei, Zeng Tao, Lin Haibo and Chen Yanqiang

    Low cycle fatigue (LCF) behaviors of pre-corroded Q345R steel under different corrosion environments were investigated where both concentration of H2S solution and pre-corrosion time served as two environmental factors. Low cycle fatigue tests were conducted at room temperature in air after the specimens were pre-corroded in H2S solution. The low cycle fatigue behaviours of pre-corrosion test material, such as strain-life relationships and cyclic stress-strain responses were investigated and compared. Results show that environmental factors had little effect on the cyclic stress response while it had much effect on the fatigue life. And pre-corrosion time had more significant effect on low cycle fatigue life of test material than the solution concentration of H2S. Furthermore, the fracture surfaces of the fatigue samples were characterized by scanning electron microscope (SEM) and the.. Read More»
    DOI: 10.4172/2169-0022.1000367

    Abstract PDF

Relevant Topics

Google Scholar citation report
Citations: 3677

Journal of Material Sciences & Engineering received 3677 citations as per Google Scholar report

Journal of Material Sciences & Engineering peer review process verified at publons

Indexed In

 
arrow_upward arrow_upward