Melt infiltration casting of alumina, silicon carbide and boron carbide reinforced aluminium matrix composites
..

Journal of Material Sciences & Engineering

ISSN: 2169-0022

Open Access

Melt infiltration casting of alumina, silicon carbide and boron carbide reinforced aluminium matrix composites


9th World Congress on Materials Science and Engineering

June 12-14, 2017 Rome, Italy

Ali Kalkanli

Middle East Technical University, Turkey

Scientific Tracks Abstracts: J Material Sci Eng

Abstract :

A series of metal matrix composites were produced using 7075 and 7085 aluminum alloys as matrix alloys and Al2O3, SiC and B3C4 seramic preforms. Melt infiltration casting was performed with a vertical squeeze caster applying 70 ton pressure during processing. Sintering of ceramic preforms were carried out at 1000, 1100 and 1300Ă?ÂșC for one hour then preheated hot sintered preforms at 1000Ă?ÂșC were placed into a die cavity before aluminum infiltration casting. During processing vertical 70 ton and upward 40 ton hold down pressure was applied for three minutes for melt infiltration. Mechanical characterizations were done by three point bending tests and flexure strength values obtains for 7075 alloy infiltrated Al2O3 preforms as 520-600 MPa.

Biography :

Ali Kalkanlihas has his expertise in processing of aluminum, magnesium alloys and metal matrix composites. He completed his MS thesis on metal powder atomization at METU Turkey and PhD thesis on melt overflow stainless steel strip casting processing in Milton Keynes at Open University, England. Alloy development and various casting and metal processes are his main interest areas.

Email: kalkanli@metu.edu.tr

Google Scholar citation report
Citations: 3677

Journal of Material Sciences & Engineering received 3677 citations as per Google Scholar report

Journal of Material Sciences & Engineering peer review process verified at publons

Indexed In

 
arrow_upward arrow_upward