Solventless synthesis of antimony sulfide, bismuth sulfide, and antimony-bismuth sulfide solid solutions using novel single source route
..

Journal of Material Sciences & Engineering

ISSN: 2169-0022

Open Access

Solventless synthesis of antimony sulfide, bismuth sulfide, and antimony-bismuth sulfide solid solutions using novel single source route


7th International Conference on Smart Materials and Structures

July 02-03, 2018 | Vienna, Austria

Tahani Alqahtani, Malik Dilshad Khan and Paul O�Brien

The University of Manchester, UK

Posters & Accepted Abstracts: J Material Sci Eng

Abstract :

Antimony(III) ethylxanthate [Sb(S2COEt)3] and bismuth(III) ethylxanthate [Bi(S2COEt)3] were used as a single source precursors for the preparation of Sb2S3 and Bi2S3, respectively, by a melt method at different temperatures. In addition, the thermogravimetric analysis reveals that both precursors exhibit complete decomposition in similar temperature range. Therefore, the mixture of these precursors can be used to produce solid solutions of Bi-Sb-S between the two phases (Bi2S3 and Sb2S3). A series with varying stoichiometry was synthesized by using different molar ratios (i.e. Sb/Sb+Bi=0.2, 0.4, 0.6 and 0.8). The XRD peaks at all ratios correspond well to the orthorhombic crystals, where the peaks fall in between those of orthorhombic Bi2S3 and orthorhombic Sb2S3 for Bi-Sb-S system. The gradual splitting and shift in the peaks position confirms the successful incorporation of antimony into bismuth sulfide. The inclusion of antimony was further confirmed by change in lattice parameters and is in good agreement with the literature values. A decrease of almost 3.5% in volume was observed as moving from Bi2S3 to Sb2S3. A change in all lattice parameters indicates that the substitution is random and not in any specific direction. The elemental compositions of all the samples were examined via energy-dispersive X-ray spectroscopy (EDX) analysis and Inductively coupled plasma�optical emission spectrometry (ICP-OES), which shows uniform distribution of elements in all samples. The morphology for all the samples was observed using SEM, revealing different morphologies as the composition changes from Bi2S3 to Sb2S3.

Google Scholar citation report
Citations: 3677

Journal of Material Sciences & Engineering received 3677 citations as per Google Scholar report

Journal of Material Sciences & Engineering peer review process verified at publons

Indexed In

 
arrow_upward arrow_upward