Synthesis and characterization of DABCO-functionalized polysulfones as anion-exchange membranes for fuel cells applications
..

Journal of Material Sciences & Engineering

ISSN: 2169-0022

Open Access

Synthesis and characterization of DABCO-functionalized polysulfones as anion-exchange membranes for fuel cells applications


5th World Congress on Materials Science & Engineering

June 13-15, 2016 Alicante, Spain

Maria Teresa Perez Prior, Monika Tannenberg, Alejandro Varez and Belen Levenfeld

Universidad Carlos III de Madrid, Spain

Scientific Tracks Abstracts: J Material Sci Eng

Abstract :

In the near past decades, there has been increasing interest in the development of anion-exchange membrane fuel cells (AEMFCs) because of their advantages such as faster oxygen reduction reaction kinetics or desirable applicability of nonprecious metals as catalyst compared to proton-exchange membrane fuel cells (PEMFCs). Anion-exchange membranes (AEM) are one of the key components in a fuel cell. Polysulfone derivatives are considered as good candidates for the preparacion of this type of materials. The efficiency of the AEM can be discussed in terms of polymeric backbone, responsible for the mechanical properties and also the anion-exchangeable group. In this work, 1,4-diazabicyclo[2,2,2]octane (DABCO) was used as quaternization agent and a series of DABCO-functionalized polysulfones were prepared. In the DABCO structure the imposibility to reach an antiperiplanar conformation minimizes the Hofmann elimination. In addition, the presence of two nitrogen atoms in the rings can stabilize the positive charge, preventing the polymer degradation. Thus, the resulting membranes showed high thermal stability for typical fuel cell operation temperatures below 100Ă?ÂșC and good alkaline stability after being treated in a 1M KOH solution for 96 h. When DABCO groups were inserted into the polymer backbone, the glass transition temperature of the functionalized membranes increased due to the incorporation of bulky substituents which decreases the mobility of the polymer chain. The ionic conductivity of these membranes is the same order of magnitude that of AEMs commonly used for this purpose. Therefore this material could be used as solid electrolyte in low temperature fuel cells.

Biography :

María Teresa Pérez Prior received her PhD in Chemistry from the University of Salamanca. She did a stage at the Fakultät für Chemie, Ruhr-Universität Bochum, Germany and a Post-doctoral stage at the Polytechnic School of Albacete, University of Castilla-La Mancha. She currently serves as Lecturer in the department of Materials Science and Engineering and Chemical Engineering at the University Carlos III of Madrid. In recent years, her main research is focused in the synthesis and characterization of polymeric materials for energy applications.

Email: maperezp@ing.uc3m.es

Google Scholar citation report
Citations: 3677

Journal of Material Sciences & Engineering received 3677 citations as per Google Scholar report

Journal of Material Sciences & Engineering peer review process verified at publons

Indexed In

 
arrow_upward arrow_upward